Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 44 g/10min |
| Melt volume flow rate | | ISO 1133 | 48.0 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.10-0.50 % |
| Water absorption rate | | ISO 62 | 0.010 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.530 |
| transmissivity | | ISO 13468-2 | 91.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1A/1 | 3200 Mpa |
| tensile strength | | ISO 527-2/1A/50 | 46.0 Mpa |
| Tensile strain | | ISO 527-2/1A/50 | 1.7 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 13 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | >1.0E+16 ohms·cm |
| relative permittivity | | IEC 60250 | 2.35 |
| relative permittivity | | IEC 60250 | 2.35 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 127 °C |
| Glass Transition Temperature | | ISO 11357-2 | 134 °C |
| vicat | | ISO 306/B50 | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.