Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 5013 JAPAN POLYPLASTIC
TOPAS®
LCD application、Optical applications
Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | JAPAN POLYPLASTIC/5013 |
|---|---|---|---|
| Glass Transition Temperature | ISO11357-2 | 134 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 127 °C |
| Vicat Softening Temperature | ISO306/B50 | 135 °C |
| Physical | Test Condition | Test Method | JAPAN POLYPLASTIC/5013 |
|---|---|---|---|
| Modeling Shrinkage | 内部方法 | 0.10到0.50 % | |
| Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 48.0 cm3/10min |
| Melt Mass-Flow Rate | 260°C/2.16kg | ISO1133 | 44 g/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.010 % |
| Mechanical Properties | Test Condition | Test Method | JAPAN POLYPLASTIC/5013 |
|---|---|---|---|
| Tensile Stress | 屈服 | ISO527-2/1A/50 | 46.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/1A/50 | 1.7 % |
| Tensile Modulus | ISO527-2/1A/1 | 3200 Mpa |
| Optical | Test Condition | Test Method | JAPAN POLYPLASTIC/5013 |
|---|---|---|---|
| Transmittance | ISO13468-2 | 91.0 % | |
| Index of Refraction | ISO489 | 1.530 |
| Impact Properties | Test Condition | Test Method | JAPAN POLYPLASTIC/5013 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 13 kJ/m² |
| Flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/5013 |
|---|---|---|---|
| Flame Rating | 1.6mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | JAPAN POLYPLASTIC/5013 |
|---|---|---|---|
| Volume Resistivity | IEC60093 | >1.0E+16 ohms·cm | |
| Comparative Tracking Index | IEC60112 | >600 V | |
| Relative Permittivity | 1kHz | IEC60250 | 2.35 |
| 10kHz | IEC60250 | 2.35 |