PEEK LNP™ THERMOCOMP™ LC006EX1-BKNAT
110
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 0.10 % | |
| ASTMD955 | 0.40 % | ||
| ISO294-4 | 0.40 % | ||
| ISO294-4 | 0.12 % | ||
| Water absorption rate | ASTMD570 | 0.080 % | |
| ISO62 | 0.070 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| FlameRating | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Wear factor - Washer | ASTMD3702Modified | 55.0 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ASTMD638 | 30800 Mpa | |
| ISO527-2/1 | 24700 Mpa | ||
| tensile strength | ASTMD638 | 226 Mpa | |
| Tensile stress | ISO527-2 | 230 Mpa | |
| elongation | ASTMD638 | 1.5 % | |
| Tensile strain | ISO527-2 | 1.5 % | |
| Flexural modulus | ASTMD790 | 20200 Mpa | |
| ISO178 | 24300 Mpa | ||
| bending strength | ASTMD790 | 325 Mpa | |
| Bending stress | ISO178 | 347 Mpa | |
| ASTMD3702Modified | 0.30 | ||
| ASTMD3702Modified | 0.32 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | ISO180/1A | 7.8 kJ/m² | |
| UnnotchedIzodImpactStrength3 | ISO180/1U | 43 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 12.5 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTME831 | 1.2E-05 cm/cm/°C | ||
| ISO11359-2 | 1.2E-05 cm/cm/°C | ||
| ASTME831 | 2.9E-05 cm/cm/°C | ||
| ISO11359-2 | 2.9E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTMD648 | >299 °C | |
| Hot deformation temperature 4 | ISO75-2/Bf | >240 °C | |
| Heat distortion temperature | ASTMD648 | >299 °C | |
| Hot deformation temperature 4 | ISO75-2/Af | >240 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.