PEEK LC006EX1-BKNAT SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™ 
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LC006EX1-BKNAT
Suspended wall beam without notch impact strength23°CISO 180/1U43 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A7.8 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D376312.5 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LC006EX1-BKNAT
Tensile modulusISO 527-2/124700 Mpa
bending strengthASTM D790325 Mpa
Wear factorWasherASTM D3702Modified55.0 10^-10in^5-min/ft-lb-hr
tensile strength 断裂ASTM D638226 Mpa
断裂ISO 527-2230 Mpa
Flexural modulusASTM D79020200 Mpa
Tensile modulusASTM D63830800 Mpa
elongation断裂ASTM D6381.5 %
bending strengthISO 178347 Mpa
coefficient of frictionStaticASTM D3702Modified0.32
Tensile strain断裂ISO 527-21.5 %
Flexural modulusISO 17824300 Mpa
coefficient of frictionDynamicASTM D3702Modified0.30
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LC006EX1-BKNAT
UL flame retardant rating0.77mmUL 94V-0
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/LC006EX1-BKNAT
Shrinkage rateMD:24小时ISO 294-40.12 %
MD:24小时ASTM D9550.10 %
Water absorption rate24hr,50%RHASTM D5700.080 %
平衡,23°C,50%RHISO 620.070 %
Shrinkage rateTD:24hrASTM D9550.40 %
TD:24小时ISO 294-40.40 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LC006EX1-BKNAT
Heat distortion temperature0.45MPa,Unannealed,64.0mmSpan,HDTISO 75-2/Bf>240 °C
Linear coefficient of thermal expansionTD:-40到40°CASTME8312.9E-05 cm/cm/°C
TD:-40到40°CISO 11359-22.9E-05 cm/cm/°C
MD:-40到40°CASTME8311.2E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,3.20mm,HDTASTM D648>299 °C
Linear coefficient of thermal expansionMD:-40到40°CISO 11359-21.2E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,64.0mm跨距,HDTISO 75-2/Af>240 °C
1.8MPa,未退火,3.20mm,HDTASTM D648>299 °C