Polyester, TS

Polyester, TS SUPRAPLAST® UPA 54 RASCHIG GmbH

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	Compression Molded	ISO 179/1eA	2.5to3.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Injection	ISO 179/1eA	3.5to5.0 kJ/m²
Impact strength of simply supported beam without notch	Compression Molded	ISO 179/1eU	5.0to10 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Injection	ISO 179/1eU	8.0to11 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index		IEC 60695-2-12	960 °C
UL flame retardant rating	1.5mm	UL 94	V-0
Hot filament ignition temperature		IEC 60695-2-13	850 °C

mechanical properties	Test Condition	Test Method	Test Result
Compressive stress		ISO 604	150to200 MPa
bending strength	Injection	ISO 178	100to120 MPa
bending strength	bending strength	Compression Molded	ISO 178	80.0to100 MPa
Bending modulus	Injection	ISO 178	13000to16000 MPa
Bending modulus	Bending modulus	Compression Molded	ISO 178	10000to13000 MPa
tensile strength	Injection	ISO 527-2	40.0to70.0 MPa
tensile strength	tensile strength	CompressionMolded	ISO 527-2	35.0to60.0 MPa
Tensile modulus	Injection	ISO 527-2	9000to11000 MPa
Tensile modulus	Tensile modulus	Compression Molded	ISO 527-2	9000to11000 MPa

thermal performance	Test Condition	Test Method	Test Result
Maximum operating temperature	20,000h	IEC 60216	170 °C
Maximum operating temperature	Maximum operating temperature	<50h	IEC 60216	220 °C
thermal conductivity		ASTME1461	0.90to1.1 W/m/K
Linear coefficient of thermal expansion	MD：50to100°C	ISO 11359-2	1.0E-5到2.0E-5 cm/cm/°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	>200 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 2577	<0.10 %
density		ISO 1183	1.90to2.10 g/cm³
Apparent density		ISO 60	0.70to0.80 g/cm³
Shrinkage rate	MD：--2	ISO 2577	0.30to0.60 %
Shrinkage rate	Shrinkage rate	MD：--3	ISO 2577	0.20to0.50 %
Water absorption rate	23°C,24hr	ISO 62	<0.50 %

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	PLC 4
Dissipation factor	1MHz	IEC 60250	0.010to0.030
Dissipation factor	Dissipation factor	100Hz	IEC 60250	0.010to0.030
Relative permittivity	1MHz	IEC 60250	4.005.00
Relative permittivity	Relative permittivity	100Hz	IEC 60250	5.006.00
Dielectric strength		IEC 60243-1	25to35 kV/mm
Volume resistivity		IEC 60093	1.0E+14到1.0E+15 ohms·cm
Surface resistivity		IEC 60093	1.0E+13到1.0E+14 ohms
Compared to the anti leakage trace index		IEC 60112	PLC 0

Supplementary Information	Test Condition	Test Method	Test Result
Compression molding pressure			>10.0 MPa
Compression molding temperature			165to180 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.