Polyester, TS SUPRAPLAST® UPA 54 RASCHIG GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodRASCHIG GmbH/SUPRAPLAST® UPA 54
Impact strength of simply supported beam without notch注塑ISO 179/1eU8.0to11 kJ/m²
模压成型ISO 179/1eU5.0to10 kJ/m²
Charpy Notched Impact Strength模压成型ISO 179/1eA2.5to3.5 kJ/m²
注塑ISO 179/1eA3.5to5.0 kJ/m²
Supplementary InformationTest ConditionTest MethodRASCHIG GmbH/SUPRAPLAST® UPA 54
Compression molding pressure>10.0 MPa
Compression molding temperature165to180 °C
Electrical performanceTest ConditionTest MethodRASCHIG GmbH/SUPRAPLAST® UPA 54
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
dielectric strengthIEC 60243-125to35 kV/mm
Volume resistivityIEC 600931.0E+14到1.0E+15 ohms·cm
relative permittivity100HzIEC 602505.006.00
Dissipation Factor100HzIEC 602500.010to0.030
arc resistanceASTM D495PLC 4
relative permittivity1MHzIEC 602504.005.00
Surface ResistivityIEC 600931.0E+13到1.0E+14 ohms
Dissipation Factor1MHzIEC 602500.010to0.030
Mechanical propertiesTest ConditionTest MethodRASCHIG GmbH/SUPRAPLAST® UPA 54
tensile strength CompressionMoldedISO 527-235.0to60.0 MPa
bending strength注塑ISO 178100to120 MPa
Flexural modulus注塑ISO 17813000to16000 MPa
compression stressISO 604150to200 MPa
Tensile modulus模压成型ISO 527-29000to11000 MPa
Flexural modulus模压成型ISO 17810000to13000 MPa
tensile strength 注塑ISO 527-240.0to70.0 MPa
bending strength模压成型ISO 17880.0to100 MPa
Tensile modulus注塑ISO 527-29000to11000 MPa
flammabilityTest ConditionTest MethodRASCHIG GmbH/SUPRAPLAST® UPA 54
Hot filament ignition temperatureIEC 60695-2-13850 °C
UL flame retardant rating1.5mmUL 94V-0
Burning wire flammability indexIEC 60695-2-12960 °C
physical property Test ConditionTest MethodRASCHIG GmbH/SUPRAPLAST® UPA 54
Shrinkage rateISO 2577<0.10 %
MD：--2ISO 25770.30to0.60 %
Apparent densityISO 600.70to0.80 g/cm³
Shrinkage rateMD：--3ISO 25770.20to0.50 %
Water absorption rate23°C,24hrISO 62<0.50 %
densityISO 11831.90to2.10 g/cm³
Thermal performanceTest ConditionTest MethodRASCHIG GmbH/SUPRAPLAST® UPA 54
maximum service temperature20,000hIEC 60216170 °C
Linear coefficient of thermal expansionMD：50到100°CISO 11359-21.0E-5到2.0E-5 cm/cm/°C
Heat distortion temperature8.0MPa,未退火，HDTISO 75-2/C>200 °C
thermal conductivityASTME14610.90to1.1 W/m/K
maximum service temperature<50hIEC 60216220 °C