Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.24 g/cm3 |
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| Water absorption rate | | ISO 62 | 0.15 % |
| Shrinkage rate | | ISO 2557 | 0.50-0.70 % |
| density | | ISO1183 | 1.24 g/cm³ |
| Shrinkage rate | | | 0.50 % |
| Water absorption rate | | ISO62 | 0.15 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC60695-2-13 | 960 °C |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/5 | 2500 MPa |
| Tensile stress | | ISO527-2/5 | 60.0 MPa |
| Tensile strain | | ISO527-2/5 | 40 % |
| Tensile modulus | | ISO 527-2 | 2500 MPa |
| Impact strength of cantilever beam gap | | ISO 180/1A | 30.0 KJ/m2 |
| Tensile fracture stress | | ISO 527-2 | 60.0 MPa |
| Tensile fracture strain | | ISO 527-2 | >30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/1A | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 250 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 140 °C |
| | ISO75-2/A | 130 °C |
| | ISO 75-2/B | 136 ℃ |
| | ISO 75-2/A | 130 ℃ |
| vicat | | ISO 306/B | 153 ℃ |
| UL flame retardant rating | | UL 94 | V-0 |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 ℃ |
| vicat | | ISO306/B | 153 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare