PC 10F13500 4Plas
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest Method4Plas/ 10F13500
Impact strength of cantilever beam gap-30°CISO 180/1A15 kJ/m²
23°CISO 180/1A30 kJ/m²
Mechanical propertiesTest ConditionTest Method4Plas/ 10F13500
Tensile strain断裂,23°CISO 527-2/540 %
23℃，断裂ISO 527-2>30 %
tensile strength 断裂,23°CISO 527-2/560.0 MPa
Tensile stress23℃，断裂ISO 527-260.0 MPa
Tensile modulus23℃ISO 527-22500 MPa
23°CISO 527-2/52500 MPa
Impact strength of cantilever beam gap23℃ISO 180/1A30.0 KJ/m2
Electrical performanceTest ConditionTest Method4Plas/ 10F13500
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
flammabilityTest ConditionTest Method4Plas/ 10F13500
Hot filament ignition temperature2.0mmIEC 60695-2-13960 °C
UL flame retardant rating3.2mmUL 94V-0
1.6mmUL 94V-0
physical property Test ConditionTest Method4Plas/ 10F13500
densityISO 11831.24 g/cm3
Water absorption rate饱和,23℃ISO 620.15 %
melt mass-flow rateISO 113315 g/10min
Shrinkage rateMD0.50 %
Water absorption rate平衡,23°C,50%RHISO 620.15 %
densityISO 11831.24 g/cm³
Shrinkage rateMDISO 25570.50-0.70 %
Thermal performanceTest ConditionTest Method4Plas/ 10F13500
Heat distortion temperature1.8MPa, 未退火，HDTISO 75-2/A130 ℃
vicatISO 306/B153 °C
ISO 306/B153 ℃
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B140 °C
1.8MPa,未退火，HDTISO 75-2/A130 °C
0.45MPa, 未退火，HDTISO 75-2/B136 ℃
UL flame retardant rating1.60mmUL 94V-0
Hot filament ignition temperature2.00mmIEC 60695-2-13960 ℃