PA66 R2000 GYMDNAT SABIC INNOVATIVE MEXICO

Form：Granules

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1700	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C4	ISO 180/1U	140	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2410	Mpa
tensile strength	Yield	ASTM D638	56.0	Mpa
	tensile strength	Break	ASTM D638	55.0	Mpa
	tensile strength	tensile strength	Break	ISO 527-2	53.0	Mpa
elongation	Yield	ASTM D638	14	%
	elongation	Break	ASTM D638	27	%
	elongation	elongation	Break	ISO 527-2	32	%
Bending modulus	--	ASTM D790	2310	Mpa
Bending modulus	Bending modulus	--	ISO 178	2000	Mpa
bending strength	--	ASTM D790	82.0	Mpa
bending strength	bending strength	--	ISO 178	65.0	Mpa
Friction coefficient	Dynamic	ASTM D3702	0.36
Friction coefficient	Friction coefficient	Static	ASTM D3702	0.27
Wear factor		ASTM D3702	1.0E+7	10^-8 mm³/N·m
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
drying time			4.0	hr
Suggested maximum moisture content			0.15 to 0.25	%
Temperature at the rear of the barrel			265 to 275	°C
Temperature in the middle of the barrel			280 to 295	°C
Temperature at the front of the material cylinder			295 to 305	°C
Processing (melt) temperature			270 to 280	°C
Mold temperature			80 to 95	°C
Back pressure			0.200 to 0.300	Mpa
Screw speed			30 to 60	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	77.0	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span4	ISO 75-2/Af	85.0	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.7E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	1.0E-4	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	Flow : 24hr	ASTM D955	1.8 - 2.2	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	2.1 - 3.1	%
Water absorption rate	24 hr, 50% RH	ASTM D570	0.25	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.