| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 253 °C |
| Glass Transition Temperature | | ISO 11357-2 | 105 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 8E-05 cm/cm/°C |
| melting temperature | | ISO 11357-3 | 285 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| ThermalConductivityofMelt | | 内部方法 | 0.20 W/m/K |
| Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 30.0 cm³/10min |
| shrinkage rate | TD | ISO 294-4 | 0.80 % |
| shrinkage rate | MD | ISO 294-4 | 0.30 % |
| DensityMelt | | 内部方法 | 1.140 g/cm³ |
| SpecificHeatCapacity of Melt | | 内部方法 | 1470 J/kg/°C |
| density | | ISO 1183 | 1.38 g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| surface resistivity | | IEC 60093 | >1.0E+15 ohms |
| volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 41 kV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| flexural modulus | 23°C | ISO 178 | 5800 MPa |
| bending strength | 23°C | ISO 178 | 155 MPa |
| tensile modulus | | ISO 527-2/1A/1 | 6400 MPa |
| tensile strength | Break | ISO 527-2/1A/5 | 100 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 2.3 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 6000 MPa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 4600 MPa |
| impact performance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 30 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.