PCT Thermx® CG023 CELANESE USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | CELANESE USA/Thermx® CG023 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
-30°C | ISO 179/1eA | 7.0 kJ/m² | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 30 kJ/m² |
Mechanical properties | Test Condition | Test Method | CELANESE USA/Thermx® CG023 |
---|---|---|---|
Flexural modulus | 23°C | ISO 178 | 5800 MPa |
Tensile modulus | ISO 527-2/1A/1 | 6400 MPa | |
Tensile creep modulus | 1hr | ISO 899-1 | 6000 MPa |
tensile strength | 断裂 | ISO 527-2/1A/5 | 100 MPa |
Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.3 % |
Tensile creep modulus | 1000hr | ISO 899-1 | 4600 MPa |
bending strength | 23°C | ISO 178 | 155 MPa |
Electrical performance | Test Condition | Test Method | CELANESE USA/Thermx® CG023 |
---|---|---|---|
dielectric strength | IEC 60243-1 | 41 kV/mm | |
Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
flammability | Test Condition | Test Method | CELANESE USA/Thermx® CG023 |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | CELANESE USA/Thermx® CG023 |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 0.80 % |
SpecificHeatCapacity of Melt | 内部方法 | 1470 J/kg/°C | |
Shrinkage rate | MD | ISO 294-4 | 0.30 % |
ThermalConductivityofMelt | 内部方法 | 0.20 W/m/K | |
DensityMelt | 内部方法 | 1.140 g/cm³ | |
density | ISO 1183 | 1.38 g/cm³ | |
Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 30.0 cm³/10min |
Thermal performance | Test Condition | Test Method | CELANESE USA/Thermx® CG023 |
---|---|---|---|
melting temperature | ISO 11357-3 | 285 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 253 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3E-05 cm/cm/°C |
TD | ISO 11359-2 | 8E-05 cm/cm/°C | |
Glass Transition Temperature | ISO 11357-2 | 105 °C |