Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.15to1.49 g/cm³ |
| spiral flow length | | | 58.4to87.0 cm |
| Shrinkage rate | | ASTM D955 | 0.35to0.36 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 60to80 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 1890to2420 MPa |
| tensile strength | | ASTM D638 | 29.6to46.6 MPa |
| elongation | | ASTM D638 | 15to380 % |
| Flexural modulus | | ASTM D790 | 1890to2840 MPa |
| bending strength | | ASTM D790 | 48.3to93.1 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 27to960 J/m |
| Dart impact | | ASTM D4226 | 50.4to178 J/cm |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 8.00to71.9 kN/m |
| aging | Test Condition | Test Method | Test Result |
|---|
| volume change | | ASTM D471 | -26--0.30 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 76.0to90.6 °C |
| Heat distortion temperature | | ASTM D648 | 83.9to92.4 °C |
| Heat distortion temperature | | ASTM D648 | 72.4to85.1 °C |
| Heat distortion temperature | | ASTM D648 | 73.0to88.0 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3.0E-5到1.4E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.