PC+PET Makroblend® UT235 M
0
- Properties:Fillermineral filler15%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.50to0.60 % | |
| Water absorption rate | ISO 62 | 0.40 % | |
| ISO 62 | 0.20 % | ||
| density | ISO 1183 | 1.34 g/cm³ | |
| Melt volume flow rate | ISO 1133 | 39.0 cm³/10min | |
| Shrinkage rate | ISO 2577 | 0.50to0.60 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO 527-2/5 | 4.0 % | |
| Flexural modulus | ISO 178 | 4650 MPa | |
| bending strength | ISO 178 | 115 MPa | |
| ISO 178 | 110 MPa | ||
| Tensile modulus | ISO 527-2/1 | 4500 MPa | |
| tensile strength | ISO 527-2/5 | 68.0 MPa | |
| ISO 527-2/5 | 67.0 MPa | ||
| Bending Strain | ISO 178 | 5.0 % | |
| Tensile strain | ISO 527-2/5 | 3.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 85 kJ/m² | |
| ISO 179/1eU | 85 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180 | 85 kJ/m² | |
| ISO 180 | 85 kJ/m² | ||
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 36.0 J | |
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 4500 N |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 114 °C | |
| vicat | ISO 306/B120 | 139 °C | |
| Heat distortion temperature | ISO 75-2/B | 128 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 4.8E-05 cm/cm/°C | |
| ISO 11359-2 | 4.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.