PC+PET Makroblend® UT235 M Covestro - Polycarbonates
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Covestro - Polycarbonates/Makroblend® UT235 M |
---|---|---|---|
Suspended wall beam without notch impact strength | 23°C | ISO 180 | 85 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 85 kJ/m² |
Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 36.0 J |
Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 4500 N |
Suspended wall beam without notch impact strength | -30°C | ISO 180 | 85 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 85 kJ/m² |
Mechanical properties | Test Condition | Test Method | Covestro - Polycarbonates/Makroblend® UT235 M |
---|---|---|---|
tensile strength | 屈服,23°C | ISO 527-2/5 | 68.0 MPa |
Tensile strain | 断裂,23°C | ISO 527-2/5 | 4.0 % |
Flexural modulus | 23°C | ISO 178 | 4650 MPa |
Bending Strain | 23°C | ISO 178 | 5.0 % |
tensile strength | 断裂,23°C | ISO 527-2/5 | 67.0 MPa |
Tensile modulus | 23°C | ISO 527-2/1 | 4500 MPa |
Tensile strain | 屈服,23°C | ISO 527-2/5 | 3.5 % |
bending strength | 3.5%Strain,23°C | ISO 178 | 110 MPa |
23°C | ISO 178 | 115 MPa |
physical property | Test Condition | Test Method | Covestro - Polycarbonates/Makroblend® UT235 M |
---|---|---|---|
Shrinkage rate | MD:270°C,3.00mm | ISO 2577 | 0.50to0.60 % |
density | 23°C | ISO 1183 | 1.34 g/cm³ |
Melt volume flow rate | 270°C/5.0kg | ISO 1133 | 39.0 cm³/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
Shrinkage rate | TD:270°C,3.00mm | ISO 2577 | 0.50to0.60 % |
Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
Thermal performance | Test Condition | Test Method | Covestro - Polycarbonates/Makroblend® UT235 M |
---|---|---|---|
Linear coefficient of thermal expansion | MD:23to85°C | ISO 11359-2 | 4.5E-05 cm/cm/°C |
vicat | ISO 306/B120 | 139 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 128 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 114 °C | |
Linear coefficient of thermal expansion | TD:23to85°C | ISO 11359-2 | 4.8E-05 cm/cm/°C |