MDPE TIPELIN® FS 383-03 MOL Petrochemicals Co. Ltd.
0
CompareTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 密度 | ISO1183 | 0.938 g/cm³ | |
| 熔体质量流动速率 | 190°C/2.16kg | ISO1133 | 0.18 g/10min |
| 190°C/21.6kg | ISO1133 | 15 g/10min | |
| 190°C/5.0kg | ISO1133 | 0.87 g/10min |
| 薄膜 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 薄膜厚度-经测试 | 70 µm | ||
| 拉伸应力 | MD:屈服,70µm,吹塑薄膜 | ISO527-3 | 24.0 MPa |
| TD:屈服,70µm,吹塑薄膜 | ISO527-3 | 19.0 MPa | |
| MD:断裂,70µm,吹塑薄膜 | ISO527-3 | 51.0 MPa | |
| TD:断裂,70µm,吹塑薄膜 | ISO527-3 | 48.0 MPa | |
| 伸长率 | MD:断裂,70µm,吹塑薄膜 | ISO527-3 | 700 % |
| TD:断裂,70µm,吹塑薄膜 | ISO527-3 | 800 % | |
| 落锤冲击 | 70µm,吹塑薄膜 | ISO7765-1/A | 100 g |
| 埃尔曼多夫抗撕强度 | MD:70µm,BlownFilm | ISO6383-2 | 0.45 N |
| TD:70µm,BlownFilm | ISO6383-2 | 3.6 N | |
| SpencerImpact-BlownFilm | 70.0µm | ASTMD3420 | 37.0 MPa |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 弯曲模量 | Compression Molded | ISO178 | 900 MPa |
| 硬度 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 肖氏硬度 | 邵氏D,模压成型 | ISO868 | 60 |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| OxidationInductionTime-CompressionMolded | 200°C | EN728 | 42 min |
| 维卡软化温度 | ISO306/A120 | 119 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.