MDPE TIPELIN® FS 383-03 MOL Petrochemicals Co. Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® FS 383-03 |
|---|---|---|---|
| Shore hardness | 邵氏D,模压成型 | ISO 868 | 60 |
| film | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® FS 383-03 |
|---|---|---|---|
| tensile strength | TD:断裂,70µm,吹塑薄膜 | ISO 527-3 | 48.0 MPa |
| SpencerImpact-BlownFilm | 70.0µm | ASTM D3420 | 37.0 MPa |
| tensile strength | TD:屈服,70µm,吹塑薄膜 | ISO 527-3 | 19.0 MPa |
| Dart impact | 70µm,吹塑薄膜 | ISO 7765-1/A | 100 g |
| film thickness | 70 µm | ||
| elongation | MD:断裂,70µm,吹塑薄膜 | ISO 527-3 | 700 % |
| Elmendorf tear strength | TD:70µm,BlownFilm | ISO 6383-2 | 3.6 N |
| tensile strength | MD:断裂,70µm,吹塑薄膜 | ISO 527-3 | 51.0 MPa |
| MD:屈服,70µm,吹塑薄膜 | ISO 527-3 | 24.0 MPa | |
| elongation | TD:断裂,70µm,吹塑薄膜 | ISO 527-3 | 800 % |
| Elmendorf tear strength | MD:70µm,BlownFilm | ISO 6383-2 | 0.45 N |
| Mechanical properties | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® FS 383-03 |
|---|---|---|---|
| Flexural modulus | 模压成型 | ISO 178 | 900 MPa |
| physical property | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® FS 383-03 |
|---|---|---|---|
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 0.87 g/10min |
| density | ISO 1183 | 0.938 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.18 g/10min |
| 190°C/21.6kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® FS 383-03 |
|---|---|---|---|
| vicat | ISO 306/A120 | 119 °C | |
| OxidationInductionTime-CompressionMolded | 200°C | EN728 | 42 min |