PBT/PC VALOX™ V3900WX-BK1H078
38
- Properties:High impactLow warpageDimensional stabilityHigh toughnessWeather resistance
- Usages:Automotive sectorCharging stationElectronic and electrical enclosureLighting applicationsCommunication equipmentWire and cable
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass Flow Rate (MFR) 266 ° C/5kg | ASTM D1238 | 35 g/10min | |
| Melt Volume Flow Rate (MVR) 265 ° C/2.16 kg | ISO 1133 | 11 cm³/10 min | |
| Longitudinal shrinkage rate (Flow) | Internal | 0.7~1 | |
| Water absorption rate | ISO 62 | 0.1 | |
| Moisture absorption rate | ISO 62 | 0.03 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | ASTM D1525 | 105 °C | |
| ISO 306 | 123 °C | ||
| ISO 306 | 121 °C | ||
| Relative Temperature Index (RTI) impact w/impact- | UL 746B | 120 °C | |
| Relative Temperature Index (RTI) Electrical Elec- | UL 746B | 120 °C | |
| Relative Temperature Index (RTI) intensity w/o impact- | UL 746B | 120 °C | |
| Coefficient of Linear Expansion (CLTE) Longitudinal (Flow) | ASTM E831 | 88.4 E-6 °C | |
| ISO 11359-2 | 88.4 E-6 °C | ||
| Coefficient of Linear Expansion (CLTE) Across Flow | ASTM E831 | 89.7 E-6 °C | |
| ISO 11359-2 | 89.7 E-6 °C | ||
| Ball indentation temperature | IEC 60695-10-2 | 75 °C | |
| IEC 60695-10-2 | 125 °C |
| combustibility | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL fire rating V-0 | UL94 | 1.5 mm | |
| UL fire rating 5VA | UL94 | 3 mm | |
| Burning wire flammability index (GWFI) 1mm | IEC 60695-2-12 | 960 passes at |
| Electrical Property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index (GWFI) 3mm | IEC 60695-2-12 | 960 passes | |
| Heating wire ignition temperature (GWIT) 1.0mm | IEC 60695-2-13 | 825 | |
| Heating wire ignition temperature (GWIT) 3.0mm | IEC 60695-2-13 | 725 by VDE | |
| UV exposure, water exposure test, and immersion | UL 746C | F1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strength yield (yld) | ASTM D638 | 53 Mpa | |
| ISO 527 | 51 Mpa | ||
| Internal | 48 Mpa | ||
| Tensile strength fracture (brk) | ISO 527 | 40 Mpa | |
| ASTM D638 | 43 Mpa | ||
| ASTM D638 | 5 | ||
| ISO 527 | 4 | ||
| ASTM D638 | 250 | ||
| ASTM D638 | 50 | ||
| ISO 527 | 42 | ||
| ASTM D790 | 80 Mpa | ||
| ISO 178 | 73 Mpa | ||
| Flexural modulus | ASTM D790 | 2200 Mpa | |
| ISO 178 | 2130 Mpa | ||
| Tensile modulus | ASTM D638 | 2200 Mpa | |
| ISO 527 | 2090 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched at 23 ℃ (73 ℉) | ISO 179/1eA | 52 kJ/m² | |
| Izod Notched -30 ℃ (-22 ℉) | ASTM D256 | 110 J/m | |
| ISO 180/1A | 8 kJ/m² | ||
| Izod Notched at 23 ℃ (73 ℉) | ASTM D256 | 800 J/m | |
| ISO 180/1A | 45 kJ/m² | ||
| ASTM D3763 | 50 J | ||
| ASTM D3763 | 50 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.