PBT/PC V3900WX-BK1H078 SABIC INNOVATIVE SHANGHAI

VALOX™

Automotive sector,Charging station,Electronic and electrical enclosure,Lighting applications,Communication equipment,Wire and cable

High impact,Low warpage,Dimensional stability,High toughness,Weather resistance

Plastic Datasheets

combustion performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
Glow wire combustion index (GWFI)	1mm	IEC 60695-2-12	960 passes at
UL fire rating V		UL 94	1.5 mm
UL flame retardant rating	5VA	UL 94	3 mm

Electrical Property	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
Glow wire combustion index (GWFI)	3mm	IEC 60695-2-12	960 passes
Glow wire ignition temperature (GWIT)	3.0mm	IEC 60695-2-13	725 by VDE
Glow wire ignition temperature (GWIT)		1.0mm	IEC 60695-2-13	825
UV exposure, water exposure test, and immersion		UL 746C	F1

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
Bending modulus	2 mm/m	ISO 178	2130 Mpa
Bending modulus		1.3 mm/m	ASTM D790	2200 Mpa
bending strength	1.3 mm，Yield	ASTM D790	80 Mpa
bending strength		2 mm/m，Yield	ISO 178	73 Mpa
elongation	Type I, 50，Yield	ASTM D638	5
elongation		50 mm/m，Yield	ISO 527	4
Elongation at Break		ASTM D638	250
		50 mm/m	ISO 527	42
		Type I, 50	ASTM D638	50
Tensile modulus	5 mm/mi	ASTM D638	2200 Mpa
Tensile modulus		1 mm/mi	ISO 527	2090 Mpa
tensile strength	Type I, 50，Break	ASTM D638	43 Mpa
		50 mm/m，Yield	ISO 527	51 Mpa
		Type I, 50，Yield	ASTM D638	53 Mpa
		50 mm/m，Break	ISO 527	40 Mpa
		Yield	Internal	48 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
melt mass-flow rate		ASTM D1238	35 g/10min
Melt Volume Flow Rate (MVR)		ISO 1133	11 cm³/10 min
Shrinkage rate	flow, 3.2	Internal	0.7-1
Water absorption rate	23°C / 50	ISO 62	0.03
Water absorption rate		23°C/sat	ISO 62	0.1

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
Charpy Notched Impact Strength	V-notch，23℃	ISO 179/1eA	52 kJ/m²
Impact strength of cantilever beam gap	30℃	ASTM D256	110 J/m
		80104，30℃	ISO 180/1A	8 kJ/m²
		80104，23℃	ISO 180/1A	45 kJ/m²
		23℃	ASTM D256	800 J/m
Instrumented dart impact energy 23 ℃ (73 ℉) total energy		ASTM D3763	50 J
Instrumented dart impact energy -40 ℃ (-40 ℉) total energy		ASTM D3763	50 J

thermal properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V3900WX-BK1H078
Ball indentation temperature	Pass	IEC 60695-10-2	125 °C
Linear coefficient of thermal expansion	-40°C to 4，Flow	ISO 11359-2	88.4 E-6 °C
		-40°C to 4，Across Flow	ISO 11359-2	89.7 E-6 °C
		-40°C to 4，Flow	ASTM E831	88.4 E-6 °C
		-40°C to 4，Across Flow	ASTM E831	89.7 E-6 °C
RTI Elec		UL 746B	120 °C
RTI Imp		UL 746B	120 °C
Vicat softening temperature	Rate B/50	ASTM D1525	105 °C
Vicat softening temperature		Rate B/5	ISO 306	123 °C