Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 10 g/10 min |
| Melt volume flow rate | | ISO 1133 | 9.00 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.40 - 0.80 % |
| Shrinkage rate | | 内部方法 | 0.40 - 0.80 % |
| Water absorption rate | | ISO 62 | 0.12 % |
| Water absorption rate | | ISO 62 | 0.090 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 87 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 82.0 % |
| Haze ratio | | ASTM D1003 | 3.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | V-2 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 850 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 850 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2180 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2300 Mpa |
| tensile strength | | ASTM D638 | 57.0 Mpa |
| tensile strength | | ISO 527-2/50 | 56.0 Mpa |
| tensile strength | | ASTM D638 | 59.0 Mpa |
| tensile strength | | ISO 527-2/50 | 55.0 Mpa |
| elongation | | ASTM D638 | 5.6 % |
| elongation | | ISO 527-2/50 | 5.4 % |
| elongation | | ASTM D638 | 120 % |
| elongation | | ISO 527-2/50 | 110 % |
| Flexural modulus | | ASTM D790 | 2180 Mpa |
| Flexural modulus | | ISO 178 | 2120 Mpa |
| bending strength | | ISO 178 | 88.0 Mpa |
| bending strength | | ASTM D790 | 92.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 60 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 无断裂 |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 无断裂 |
| Dart impact | | ASTM D3763 | 77.0 J |
| Dart impact | | ASTM D3763 | 75.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | > 1.0E+15 ohms |
| Volume resistivity | | ASTM D257 | > 1.0E+15 ohms·cm |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 3.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 40 to 60 % |
| Temperature at the rear of the barrel | | | 270 to 295 °C |
| Temperature in the middle of the barrel | | | 280 to 305 °C |
| Temperature at the front of the material cylinder | | | 295 to 315 °C |
| Spray nozzle temperature | | | 290 to 310 °C |
| Processing (melt) temperature | | | 295 to 315 °C |
| Temperature | | | 70 to 95 °C |
| Back pressure | | | 0.300 to 0.700 Mpa |
| screw speed | | | 40 to 70 rpm |
| Exhaust hole depth | | | 0.025 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 120 °C |
| Heat distortion temperature | | ISO 75-2/Af | 116 °C |
| vicat | | ASTM D152510 | 138 °C |
| vicat | | ISO 306/B120 | 139 °C |
| ball-indentation hardness | | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | | ASTM E831 | 6.7E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.7E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM E831 | 8.0E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 130 °C |
| RTI | | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.