PC EXL1414T-NA8A005T SABIC INNOVATIVE SINGAPHORE
LEXAN™ 
Bottle cap、Home appliance components、Electrical applications
Easy to process、Moderate liquidity、Ductility、Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
The impact strength of a simply supported beam without a notch is 723°CISO 179/1eU无断裂
Dart impact equipped with measuring instruments-30°C, Total EnergyASTM D376377.0 J
23°C, Total EnergyASTM D376375.0 J
Impact strength of simply supported beam gap 7-30°CISO 179/1eA60 kJ/m²
Unscented Izod Impact Strength 8-30°CISO 180/1U无断裂
The impact strength of a simply supported beam without a notch is 7-30°CISO 179/1eU无断裂
Impact strength of simply supported beam gap 723°CISO 179/1eA70 kJ/m²
Unscented Izod Impact Strength 823°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Rockwell hardnessL 计秤ISO 2039-287
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
tensile strength屈服ISO 527-2/5056.0 Mpa
Bending stress-- 5, 6ISO 17888.0 Mpa
elongation断裂ISO 527-2/50110 %
Flexural modulus-- 5ISO 1782120 Mpa
elongation屈服 3ASTM D6385.6 %
Bending stress屈服, 50.0 mm 跨距 4ASTM D79092.0 Mpa
Tensile modulus-- 2ASTM D6382180 Mpa
tensile strength屈服 3ASTM D63857.0 Mpa
断裂ISO 527-2/5055.0 Mpa
elongation屈服ISO 527-2/505.4 %
Flexural modulus50.0 mm 跨距 4ASTM D7902180 Mpa
Tensile modulus--ISO 527-2/12300 Mpa
elongation断裂 3ASTM D638120 %
tensile strength断裂 3ASTM D63859.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Volume resistivityASTM D257> 1.0E+15 ohms·cm
Surface ResistivityASTM D257> 1.0E+15 ohms
optical performance Test ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
transmissivity2540 µmASTM D100382.0 %
Haze ratio2540 µmASTM D10033.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
UL flame retardant rating3.0 mmUL 94V-2
Hot filament ignition temperature0.8 mmIEC 60695-2-13850 °C
3.0 mmIEC 60695-2-13850 °C
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
UL flame retardant rating0.8 mmUL 94HB
physical property Test ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Water absorption rate平衡, 23°C, 50% RHISO 620.090 %
Shrinkage rate横向流动 : 3.20 mm内部方法0.40 到 0.80 %
Molten Volume Flow Rate (MVR)300°C/1.2 kgISO 11339.00 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123810 g/10 min
Shrinkage rate流动 : 3.20 mm内部方法0.40 到 0.80 %
Water absorption rate饱和, 23°CISO 620.12 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
vicat--ISO 306/B120139 °C
横向 : 23 到 80°CISO 11359-28.0E-5 cm/cm/°C
Thermal deformation temperature under load1.8 MPa, 未退火, 3.20 mmASTM D648120 °C
Ball Pressure Test123 到 127°CIEC 60695-10-2通过
Thermal deformation temperature under load1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9ISO 75-2/Af116 °C
流动 : 23 到 80°CISO 11359-26.7E-5 cm/cm/°C
横向 : -40 到 95°CASTM E8318.0E-5 cm/cm/°C
RTIUL 746130 °C
vicat--ASTM D152510, ISO 306/B5010138 °C
流动 : -40 到 95°CASTM E8316.7E-5 cm/cm/°C
RTI ElecUL 746130 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Processing (melt) temperature295 到 315 °C
drying temperature120 °C
Exhaust hole depth0.025 到 0.076 mm
Temperature at the front of the material cylinder295 到 315 °C
Suggested maximum moisture content0.020 %
Temperature in the middle of the barrel280 到 305 °C
Temperature70 到 95 °C
screw speed40 到 70 rpm
Temperature at the rear of the barrel270 到 295 °C
Back pressure0.300 到 0.700 Mpa
drying time3.0 到 4.0 hr
Suggested injection volume40 到 60 %
Spray nozzle temperature290 到 310 °C