| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.70 g/cm³ |
| Shrinkage rate | | | 0.20to0.70 % |
| Water absorption rate | Equilibrium | | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 185 MPa |
| elongation | Break | | 2.8 % |
| Flexural modulus | | | 16000 MPa |
| bending strength | | | 300 MPa |
| compressive strength | | | 154 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 16.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | | 3.00 |
| Surface Resistivity | | | 2.2E+15 ohms |
| Volume resistivity | | | 8E+16 ohms·cm |
| dielectric strength | | | 18 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | | 268 °C |
| melting temperature | | | 288 °C |
| Linear coefficient of thermal expansion | | | 1.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.