Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | | 1.0 % |
| Water absorption rate | | | 7.0 % |
| Water absorption rate | | | 2.3 % |
| density | | | 1.34 g/cm³ |
| Shrinkage rate | | | 0.50to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | | 850 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | PX-2 |
| Trekking Services | | | 635.00 cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | | 74.0 MPa |
| Flexural modulus | | | 4800 MPa |
| bending strength | | | 100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | | 12 kJ/m² |
| Impact strength of simply supported beam without notch | | | 20 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | | 1E+15 ohms |
| Surface Resistivity | | | 1E+13 ohms |
| Volume resistivity | | | 1E+17 ohms·cm |
| Volume resistivity | | | 1E+15 ohms·cm |
| dielectric strength | | | 16to20 kV/mm |
| dielectric strength | | | 23to25 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | | 70.0 °C |
| melting temperature | | | 218 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare