PA6 PA CM 25-2AP Poly Plastic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Poly Plastic/PA CM 25-2AP |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | 12 kJ/m² | |
| 20°C | 20 kJ/m² |
| Supplementary Information | Test Condition | Test Method | Poly Plastic/PA CM 25-2AP |
|---|---|---|---|
| Trekking Services | KIT | 635.00 cm | |
| UL flame retardant rating | 2.00mm | PX-2 |
| Mechanical properties | Test Condition | Test Method | Poly Plastic/PA CM 25-2AP |
|---|---|---|---|
| Flexural modulus | 23°C | 4800 MPa | |
| bending strength | 100 MPa | ||
| tensile strength | 屈服 | 74.0 MPa |
| Electrical performance | Test Condition | Test Method | Poly Plastic/PA CM 25-2AP |
|---|---|---|---|
| Volume resistivity | --3 | 1E+15 ohms·cm | |
| --2 | 1E+17 ohms·cm | ||
| Surface Resistivity | --3 | 1E+13 ohms | |
| --2 | 1E+15 ohms | ||
| dielectric strength | --3 | 16to20 kV/mm | |
| --2 | 23to25 kV/mm |
| flammability | Test Condition | Test Method | Poly Plastic/PA CM 25-2AP |
|---|---|---|---|
| Hot filament ignition temperature | 850 °C |
| physical property | Test Condition | Test Method | Poly Plastic/PA CM 25-2AP |
|---|---|---|---|
| Shrinkage rate | 0.50to0.70 % | ||
| Water absorption rate | 饱和,23°C | 7.0 % | |
| density | 1.34 g/cm³ | ||
| Water absorption rate | 平衡,23°C,50%RH | 2.3 % | |
| 23°C,24hr | 1.0 % |
| Thermal performance | Test Condition | Test Method | Poly Plastic/PA CM 25-2AP |
|---|---|---|---|
| melting temperature | 218 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | 70.0 °C |