ASA+PC Luran® S KR2861/1C INEOS Barex
0
- Properties:Mechanical properties
- Usages:Applications and Enclosures in the Automotive Industry
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| 弯曲应力 | ISO178 | 78.0 MPa | |
| 伸长率 | Break | ISO527-3 | >50 % |
| 密度 | ISO1183 | 1.15 g/cm³ | |
| 熔体体积流动速率 | 220°C/10.0kg | ISO1133 | 3.50 cm³/10min |
| 260°C/5.0kg | ISO1133 | 14.0 cm³/10min | |
| 收缩率 | ISO294-4 | 0.50到0.90 % | |
| 简支梁缺口冲击强度 | -30°C | ISO179 | 20 kJ/m² |
| 23°C | ISO179 | 60 kJ/m² | |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/A | 15 kJ/m² |
| 23°C | ISO180/A | 60 kJ/m² | |
| 热变形温度 | 0.45MPa,退火 | ISO75-2/B | 125 °C |
| 1.8MPa,退火 | ISO75-2/A | 106 °C | |
| 表面电阻率 | IEC60093 | 1E+13 ohms | |
| 体积电阻率 | IEC60093 | 1E+14 ohms·cm | |
| 介电常数 | 100Hz | IEC60250 | 3.40 |
| 耗散因数 | 100Hz | IEC60250 | 6E-03 |
| 1MHz | IEC60250 | 0.015 | |
| 维卡软化温度 | -- | ISO306/A50 | 136 °C |
| -- | ISO306/B50 | 120 °C | |
| 线性热膨胀系数 | MD | ISO11359-2 | 7.0E-5到9.0E-5 cm/cm/°C |
| 导热系数 | DIN52612 | 0.17 W/m/K | |
| 吸水率 | 饱和,23°C | ISO62 | 0.90 % |
| 平衡,23°C,50%RH | ISO62 | 0.25 % | |
| 球压硬度 | ISO2039-1 | 95.0 MPa | |
| 拉伸模量 | ISO527-2 | 2300 MPa | |
| 拉伸应力 | 屈服,23°C | ISO527-2 | 53.0 MPa |
| 拉伸应变 | 屈服,23°C | ISO527-2 | 4.9 % |
| 拉伸蠕变模量 | 1hr | ISO899-1 | 2000 MPa |
| 1000hr | ISO899-1 | 1600 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.