Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA+PC Luran® S KR2861/1C INEOS Barex
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | INEOS Barex/Luran® S KR2861/1C | |
|---|---|---|---|
| vicat | -- | ISO 306/B50 | 120 °C |
| ball-indentation hardness | ISO 2039-1 | 95.0 MPa | |
| density | ISO 1183 | 1.15 g/cm³ | |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 125 °C |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 15 kJ/m² |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 14.0 cm³/10min |
| bending strength | ISO 178 | 78.0 MPa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 53.0 MPa |
| Tensile modulus | ISO 527-2 | 2300 MPa | |
| elongation | 断裂 | ISO 527-3 | >50 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 3.50 cm³/10min |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7.0E-5到9.0E-5 cm/cm/°C |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Tensile creep modulus | 1hr | ISO 899-1 | 2000 MPa |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 60 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 60 kJ/m² |
| Shrinkage rate | ISO 294-4 | 0.50to0.90 % | |
| Dissipation Factor | 100Hz | IEC 60250 | 6E-03 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| vicat | -- | ISO 306/A50 | 136 °C |
| thermal conductivity | DIN 52612 | 0.17 W/m/K | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.9 % |
| dielectric constant | 100Hz | IEC 60250 | 3.40 |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 20 kJ/m² |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.90 % |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 106 °C |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1600 MPa |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.25 % |