PC GZ2530 BK IDEMITSU JAPAN

154

Form：Granules | Grade：Injection grade

Properties:

Flame retardantGlass fiber reinforced maFiller: Glass fiber reinfPhosphorus contentLow (to none)Bromine freeFlame retardant performan30%Filler by weight30%Filler by weight

Typical Applications:

Automotive ApplicationsHome appliance componentsLCD applicationPower/Other ToolsmodelPrinting machine parts

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Home appliance components \| LCD application \| Power/Other Tools \| model \| Printing machine parts
Properties:	Flame retardant \| Glass fiber reinforced ma \| Filler: Glass fiber reinf \| Phosphorus content \| Low (to none) \| Bromine free \| Flame retardant performan \| 30% \| Filler by weight \| 30% \| Filler by weight

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	17	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.4mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	180	Mpa
tensile strength	Yield	ISO 527-2	130	Mpa
Nominal tensile fracture strain		ISO 527-2	4.0	%
Bending modulus		ISO 178	7900	Mpa
Bending modulus	Bending modulus		ISO 178	7900	Mpa
Tensile strain	Break	ISO 527-2	4	%
tensile strength	Break	ISO 527-2	130	Mpa
Rockwell hardness	M -Sale	ISO 2039-2	75
Charpy Notched Impact Strength		ISO 179	17	kJ/m²
bending strength		ISO 178	180	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.40 mm	UL 94	V-0
Linear coefficient of thermal expansion		ASTM D696	0.000023	cm/cm/℃
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	147	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	147	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.3E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.11	%
Shrinkage rate	MD:2.00mm	Internal Method	0.15	%
Shrinkage rate	Shrinkage rate	TD:2.00mm	Internal Method	0.60	%
Spiral flow length		Internal Method	16.0	CM
density		ISO 1183	1.42	g/cm³
Water absorption rate	Equilibrium, 23℃, 50% RH	ISO 62	0.11	%
Shrinkage rate	MD: 2.00 mm	Internal Method	0.15	%
Shrinkage rate	Shrinkage rate	TD	Internal Method	0.6	%
density		ISO 1183	1.42	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	9E-03
Dielectric constant	1MHz	IEC 60250	3.45
Dielectric strength		IEC 60243-1	>22	KV/mm
Dielectric strength	Dielectric strength		IEC 60243-1	> 22	KV/mm
Arc resistance		ASTM D495	110	sec
Dielectric constant	1 MHz	IEC 60250	2.95
Volume resistivity		ASTM D257	>1.0E+16	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	75
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut			>PC-GF30<

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC GZ2530 BK IDEMITSU JAPAN

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index