Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GZ2530 BK IDEMITSU JAPAN
TARFLON™
Automotive Applications、Home appliance components、LCD application、Power/Other Tools、model、Printing machine parts
Flame retardant、Glass fiber reinforced ma、Filler: Glass fiber reinf、30% filler by weight、30% filler by weight、Phosphorus content、Low (to none)、Bromine free、Flame retardant performan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/GZ2530 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179 | 17 kJ/m² |
| Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/GZ2530 BK |
|---|---|---|---|
| ISO Shortcut | >PC-GF30< |
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/GZ2530 BK |
|---|---|---|---|
| Rockwell hardness | M级 | ISO2039-2 | 75 |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/GZ2530 BK |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 4.0 % | |
| Rockwell hardness | M 计秤 | ISO 2039-2 | 75 |
| Tensile stress | 断裂 | ISO 527-2 | 130 Mpa |
| bending strength | ISO 178 | 180 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 17 kJ/m² | |
| Tensile strain | 断裂 | ISO 527-2 | 4 % |
| Flexural modulus | ISO 178 | 7900 Mpa | |
| Tensile stress | 屈服 | ISO527-2 | 130 Mpa |
| Bending stress | ISO178 | 180 Mpa | |
| Flexural modulus | ISO178 | 7900 Mpa |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/GZ2530 BK |
|---|---|---|---|
| Dissipation Factor | 1MHz | IEC60250 | 9E-03 |
| Volume resistivity | ASTMD257 | >1.0E+16 ohms·cm | |
| dielectric constant | 1 MHz | IEC 60250 | 2.95 |
| 1MHz | IEC60250 | 3.45 | |
| electric strength | IEC 60243-1 | > 22 KV/mm | |
| dielectric strength | IEC60243-1 | >22 KV/mm | |
| arc resistance | ASTM D495 | 110 sec |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/GZ2530 BK |
|---|---|---|---|
| FlameRating | 1.4mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/GZ2530 BK |
|---|---|---|---|
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.60 % |
| TD | Internal Method | 0.6 % | |
| SpiralFlow2.3 | 内部方法 | 16.0 CM | |
| Water absorption rate 4 | 平衡,23°C,50%RH | ISO62 | 0.11 % |
| density | ISO 1183 | 1.42 g/cm³ | |
| ISO1183 | 1.42 g/cm³ | ||
| Shrinkage rate | MD:2.00mm | 内部方法 | 0.15 % |
| MD: 2.00 mm | Internal Method | 0.15 % | |
| Water absorption rate | 平衡, 23℃, 50% RH | ISO 62 | 0.11 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/GZ2530 BK |
|---|---|---|---|
| UL flame retardant rating | 1.40 mm | UL 94 | V-0 |
| Linear expansion coefficient | ASTM D696 | 0.000023 cm/cm/℃ | |
| 1.8MPa,未退火 | ISO75-2/A | 147 °C | |
| MD | ISO11359-2 | 2.3E-05 cm/cm/°C | |
| 1.8 MPa, 未退火 | ISO 75-2/A | 147 °C |