Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | JIS K-7112 | 1.04-1.06 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 3-6 10 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | JIS K-7209 | 0.07-0.08 % |
| melt mass-flow rate | | JIS K-7210 | 7.0 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | JIS K-7110 | 9.0 kg-cm/cm of notch |
| Rockwell hardness | | JIS K-7202 | R109 R,MScale |
| Rubbing modulus | | JIS K-7203 | 2.4 10 |
| tensile strength | | JIS K-7113 | 270 kg/cm |
| elongation at break | | JIS K-7113 | 40 % |
| bending strength | | JIS K-7203 | 430 kg/cm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D-257 | >10 Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | JIS K-7207 | 80 °C |
| flammability | | UL 94 | HB |
| vicat | | JIS K-7206 | 90 °C |
| Linear coefficient of thermal expansion | | ASTM D-696 | 7-8 10 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.