Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.60 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| Shrinkage rate | | 内部方法 | 0.40to0.70 % |
| Shrinkage rate | | 内部方法 | 0.40to0.70 % |
| melt mass-flow rate | | ASTMD1238 | 22 g/10min |
| density | | ISO 1183 | 1.13to1.15 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 23 % |
| Burning wire flammability index | | IEC 60695-2-12 | 750 °C |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2/50 | 50 % |
| tensile strength | Yield | ISO 527-2/50 | 50.0 MPa |
| Tensile modulus | | ISO 527-2/1 | 2100 MPa |
| bending strength | | ISO 178 | 80.0 MPa |
| Flexural modulus | | ISO 178 | 2250 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 450 J/m |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| dielectric constant | | IEC 60250 | 2.90 |
| dielectric strength | | IEC 60243-1 | 24 kV/mm |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/A50 | 130 °C |
| Continuous use temperature | | IEC 60216 | 90.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 116 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| ball-indentation hardness | | IEC 60695-10-2 | 通过 |
| vicat | | ISO 306/B50 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.