Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 17 g/10min |
| Shrinkage rate | | 内部方法 | 1.8to2.2 % |
| Water absorption rate | | ASTM D570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 94 |
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 69.0 MPa |
| elongation | Break | ASTM D638 | 45 % |
| Tensile modulus | | ISO 527-2 | 3000 MPa |
| tensile strength | Yield | ISO 527-2 | 70.0 MPa |
| elongation | Break | ISO 527-2 | 40 % |
| Flexural modulus | | ASTM D790 | 2800 MPa |
| Flexural modulus | | ISO 178 | 2900 MPa |
| bending strength | | ASTM D790 | 100 MPa |
| Taber abraser | | ASTM D1044 | 13.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 78 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1.0E+16到1.0E+17 ohms |
| Volume resistivity | | ASTM D257 | 1.0E+15到1.0E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 18 kV/mm |
| dielectric constant | | ASTM D150 | 3.80 |
| Dissipation Factor | | ASTM D150 | 7E-03 |
| arc resistance | | ASTM D495 | 250 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTMD696 | 1E-04 cm/cm/°C |
| specific heat | | | 1470 J/kg/°C |
| thermal conductivity | | | 0.23 W/m/K |
| Heat distortion temperature | | ISO 75-2/B | 163 °C |
| Heat distortion temperature | | ASTM D648 | 136 °C |
| Heat distortion temperature | | ISO 75-2/A | 100 °C |
| Heat distortion temperature | | ASTM D648 | 172 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.