POM Homopolymer Tenac™ 4060 ASAHI JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 4060 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 9.0 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 78 J/m |
| hardness | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 4060 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 94 |
| R级 | ASTM D785 | 120 |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 4060 |
|---|---|---|---|
| dielectric strength | ASTM D149 | 18 kV/mm | |
| dielectric constant | 23°C,1MHz | ASTM D150 | 3.80 |
| Surface Resistivity | ASTM D257 | 1.0E+16到1.0E+17 ohms | |
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15到1.0E+16 ohms·cm |
| Dissipation Factor | 23°C,1MHz | ASTM D150 | 7E-03 |
| arc resistance | ASTM D495 | 250 sec |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 4060 |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 13.0 mg | |
| tensile strength | -- | ASTM D638 | 69.0 MPa |
| elongation | 断裂 | ASTM D638 | 45 % |
| Tensile modulus | ISO 527-2 | 3000 MPa | |
| Flexural modulus | -- | ISO 178 | 2900 MPa |
| tensile strength | 屈服 | ISO 527-2 | 70.0 MPa |
| bending strength | ASTM D790 | 100 MPa | |
| Flexural modulus | -- | ASTM D790 | 2800 MPa |
| elongation | 断裂 | ISO 527-2 | 40 % |
| flammability | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 4060 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 4060 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.8to2.2 % |
| density | ASTMD792 | 1.42 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 17 g/10min |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/Tenac™ 4060 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 136 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 172 °C | |
| thermal conductivity | 0.23 W/m/K | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 163 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C | |
| specific heat | 1470 J/kg/°C | ||
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |