PCT Thermx® CG033 CELANESE USA

Properties:
Filler
glass fiber reinforced material
30%
filler by weight
Usages:
currency
Compare

Technical Data Sheet

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa未退火	ISO 75-2/Bf	270 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.80MPa退火	ISO 75-2/Af	262 °C
vicat	玻璃转化温度	ISO 11357-2	105 °C
vicat	vicat	Melting Temperature	ISO 11357-3	283 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.2E-05 cm/cm／°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	8.5E-05 cm/cm／°C

flame retardant performance	Test Condition	Test Method	Test Result
Limiting Oxygen Index		ISO 4589-2	29 %
UL flame retardant rating		UL -94	HB 0.80mm
	UL flame retardant rating		UL -94	HB 1.50mm
	UL flame retardant rating	UL flame retardant rating		UL -94	HB 3.00mm

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.45 g/cm³
shrinkage rate	MD	ISO 294-4	0.80 %
shrinkage rate	shrinkage rate	TD	ISO 294-4	0.20 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	1E+15 Ω.cm
surface resistivity		IEC 60093	>1.0E+15 Ω.cm
dielectric strength		IEC 60243-1	33 KV/mm
Dissipation Factor	相对漏电起痕指数	IEC 60112	560 V

mechanical properties	Test Condition	Test Method	Test Result
flexural modulus	23°C	ISO 178	8000 MPa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50 kJ/m²
tensile strength	23°C	ISO 527-2	120 MPa
Elongation at break	23°C	ISO 527-2	2.0 %
tensile modulus	23°C	ISO 527-2	8500 MPa
bending strength	23°C	ISO 178	180 MPa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.