PCT Thermx® CG033 CELANESE USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/Thermx® CG033 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 8000 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 8500 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 120 MPa |
| elongation at break | 23°C | ISO 527-2 | 2.0 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| bending strength | 23°C | ISO 178 | 180 MPa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/Thermx® CG033 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 560 V |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 Ω.cm | |
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | CELANESE USA/Thermx® CG033 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 29 % | |
| UL flame retardant rating | UL -94 | HB 0.80mm | |
| UL -94 | HB 1.50mm | ||
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | CELANESE USA/Thermx® CG033 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.20 % |
| MD | ISO 294-4 | 0.80 % | |
| density | ISO 1183 | 1.45 g/cm³ |
| Thermal performance | Test Condition | Test Method | CELANESE USA/Thermx® CG033 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 262 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 8.5E-05 cm/cm／°C |
| MD | ISO 11359-2 | 3.2E-05 cm/cm／°C | |
| vicat | 熔融温度 | ISO 11357-3 | 283 °C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 270 °C |
| vicat | 玻璃转化温度 | ISO 11357-2 | 105 °C |