PC LEXAN™ FST9405T resin

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.33 g/cm³
density	density		ISO 1183	1.33 g/cm³
melt mass-flow rate		ASTM D1238	9.0 g/10min
Melt volume flow rate		ISO 1133	10.0 cm³/10min
Shrinkage rate		内部方法	0.50to0.70 %
Shrinkage rate	Shrinkage rate		内部方法	0.50to0.70 %

flammability	Test Method	Test Result
NBSSmokeDensity-Flaming,Dmax	ASTME662	<75.0
OSU peak heat release rate	FAR25.853	<55.0 kW/m²
OSU total heat release	FAR25.853	<55.0 kW·min/m²
VerticalBurnTest	FAR25.853	1.0 sec

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap		ASTM D256	85 J/m
	Impact strength of cantilever beam gap		ASTM D256	130 J/m
		Impact strength of cantilever beam gap		ISO 180/1A	9.0 kJ/m²
			Impact strength of cantilever beam gap		ISO 180/1A	12 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	11 kJ/m²
Suspended wall beam without notch impact strength		ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength		ISO 180/1U	NoBreak
Dart impact		ASTM D3763	60.0 J
Multi axis Instrumented Impact Energy		ISO 6603-2	130 J
Charpy Notched Impact Strength		ISO 179/1eA	NoBreak
	Charpy Notched Impact Strength		ISO 179/1eA	NoBreak
	Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	NoBreak
Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
Charpy Notched Impact Strength		ISO 179/1eA	NoBreak

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2600 MPa
Tensile modulus	Tensile modulus		ISO 527-2/1	2600 MPa
tensile strength	Yield	ASTM D638	77.0 MPa
	tensile strength	Yield	ISO 527-2/50	77.0 MPa
		tensile strength	Break	ASTM D638	70.0 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	70.0 MPa
elongation	Yield	ASTM D638	6.0 %
Tensile strain	Yield	ISO 527-2/50	6.0 %
elongation	Break	ASTM D638	75 %
Tensile strain	Break	ISO 527-2/50	95 %
Flexural modulus		ASTM D790	2700 MPa
Flexural modulus	Flexural modulus		ISO 178	2500 MPa
bending strength		ISO 178	105 MPa
bending strength	bending strength		ASTM D790	115 MPa

Thermal performance	Test Condition	Test Method	Test Result
vicat		ASTM D152512	114 °C
vicat	vicat		ISO 306/B120	113 °C
Linear coefficient of thermal expansion		ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	6E-05 cm/cm/°C
Heat distortion temperature		ASTM D648	105 °C
	Heat distortion temperature		ISO 75-2/Bf	94.0 °C
		Heat distortion temperature		ASTM D648	95.0 °C
		Heat distortion temperature	Heat distortion temperature		ISO 75-2/Af	104 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.