Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LEXAN™ FST9405T resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LEXAN™ FST9405T resin |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C8 | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C9 | ISO 180/1A | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C8 | ISO 179/1eU | NoBreak |
| 23°C7 | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 130 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| Impact strength of simply supported beam without notch | -30°C7 | ISO 179/1eU | NoBreak |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 130 J | |
| Charpy Notched Impact Strength | 23°C7 | ISO 179/1eA | NoBreak |
| 23°C8 | ISO 179/1eA | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 85 J/m |
| 23°C9 | ISO 180/1A | 11 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Charpy Notched Impact Strength | -30°C7 | ISO 179/1eA | NoBreak |
| Impact strength of cantilever beam gap | 23°C10 | ISO 180/1A | 12 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Charpy Notched Impact Strength | -30°C8 | ISO 179/1eA | NoBreak |
| Mechanical properties | Test Condition | Test Method | SABIC/LEXAN™ FST9405T resin |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 6.0 % |
| tensile strength | 屈服 | ASTM D638 | 77.0 MPa |
| Flexural modulus | ISO 178 | 2500 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| tensile strength | 屈服 | ISO 527-2/50 | 77.0 MPa |
| bending strength | ISO 178 | 105 MPa | |
| elongation | 断裂 | ASTM D638 | 75 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 115 MPa |
| Tensile modulus | ASTM D638 | 2600 MPa | |
| tensile strength | 断裂 | ASTM D638 | 70.0 MPa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2700 MPa |
| Tensile strain | 断裂 | ISO 527-2/50 | 95 % |
| Tensile modulus | ISO 527-2/1 | 2600 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 70.0 MPa |
| flammability | Test Condition | Test Method | SABIC/LEXAN™ FST9405T resin |
|---|---|---|---|
| OSU peak heat release rate | FAR25.853 | <55.0 kW/m² | |
| NBSSmokeDensity-Flaming,Dmax | ASTME662 | <75.0 | |
| VerticalBurnTest | 60s),passesat，Testa | FAR25.853 | 1.0 sec |
| OSU total heat release | FAR25.853 | <55.0 kW·min/m² |
| physical property | Test Condition | Test Method | SABIC/LEXAN™ FST9405T resin |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.50to0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 10.0 cm³/10min |
| density | ASTM D792 | 1.33 g/cm³ | |
| Shrinkage rate | TD | 内部方法 | 0.50to0.70 % |
| density | ISO 1183 | 1.33 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 9.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC/LEXAN™ FST9405T resin |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 94.0 °C |
| vicat | ASTM D152512 | 114 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| vicat | ISO 306/B120 | 113 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 105 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 104 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 95.0 °C |