Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Glass Fiber Content | | | 30 % |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0 % |
| Shrinkage rate | | | 0.5 % |
| Temperature | | | 90 °C |
| Melt Temperature | | | 335 °C |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 30%玻纤增强 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| CTI UL standard value | | | 4 |
| Water absorption rate | | | 0.002 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 120 J/m |
| tensile strength | | | 150 Mpa |
| Rockwell hardness | | | 108 R |
| Flexural modulus | | | 12 GPa |
| tensile strength | | | 2.7 % |
| bending strength | | | 170 Mpa |
| Charpy Notched Impact Strength | | ASTM D256/ISO 179 | 35 kg·cm/cm(J/M)ft·lb/in |
| Charpy Notched Impact Strength | | ASTM D256/ISO 179 | 40 kg·cm/cm(J/M)ft·lb/in |
| Charpy Notched Impact Strength | | ASTM D256/ISO 179 | 30 kg·cm/cm(J/M)ft·lb/in |
| elongation at break | | ASTM D638/ISO 527 | 2.7 % |
| Tensile modulus | | ASTM D638/ISO 527 | 13000 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 165 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 11000 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 190 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | | 26 MV/m |
| dielectric constant | | | 3.9 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1620 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| combustibility | | | V-0（0.2) |
| Heat distortion temperature | | | 265 ºC |
| Linear coefficient of thermal expansion | | | 1.3(3.7) 10-5k |
| Heat distortion temperature | | | 277 ºC |
| Combustibility (rate) | | UL 94 | V-0 |
| Heat distortion temperature | | ASTM D648/ISO 75 | 300 ℃（℉） |
| Heat distortion temperature | | ASTM D648/ISO 75 | 268 ℃（℉） |
| melting temperature | | | 335 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.