LCP 6130 DUPONT USA
ZENITE®
Aerospace、Electrical field、Electronic field、Household appliances、Household appliances
Flame retardant、High temperature resistan、Antistatic、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DUPONT USA/6130 |
|---|---|---|---|
| Water absorption rate | 0.002 % | ||
| CTI UL standard value | 4 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/6130 |
|---|---|---|---|
| Rockwell hardness | 108 R | ||
| bending strength | ASTM D790/ISO 178 | 190 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 120 J/m | ||
| Flexural modulus | ASTM D790/ISO 178 | 11000 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 2.7 % | ||
| bending strength | 170 Mpa | ||
| Flexural modulus | 12 GPa | ||
| Tensile modulus | ASTM D638/ISO 527 | 13000 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 30 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 2.7 % | |
| tensile strength | 150 Mpa | ||
| ASTM D638/ISO 527 | 165 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | DUPONT USA/6130 |
|---|---|---|---|
| dielectric strength | 26 MV/m | ||
| dielectric constant | 3.9 |
| other | Test Condition | Test Method | DUPONT USA/6130 |
|---|---|---|---|
| characteristic | 30%玻纤增强 |
| Physical properties | Test Condition | Test Method | DUPONT USA/6130 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1620 |
| processability | Test Condition | Test Method | DUPONT USA/6130 |
|---|---|---|---|
| Shrinkage rate | 垂直方向 | 0.5 % | |
| 流动方向 | 0 % | ||
| Melt Temperature | 335 °C | ||
| Temperature | 90 °C |
| physical property | Test Condition | Test Method | DUPONT USA/6130 |
|---|---|---|---|
| Glass Fiber Content | 30 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/6130 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | 0.46Mpa，HDT | 277 ºC | |
| HDT | ASTM D648/ISO 75 | 268 ℃（℉） | |
| combustibility | V-0（0.2) | ||
| Linear coefficient of thermal expansion | 1.3(3.7) 10-5k | ||
| melting temperature | 335 ℃（℉） | ||
| Heat distortion temperature | 1.82Mpa，HDT | 265 ºC |