Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting mixed viscosity | | ASTMD2393 | 480到720 min |
| GelTime | | ASTMD2471 | 12.0到14.0 min |
| | | 按重量计算的混合比:1.0 |
| | | 按重量计算的混合比:1.0 |
| Thermosetting mixed viscosity | | ASTMD2393 | 3000 cP |
| Thermosetting mixed viscosity | | ASTMD2393 | 4500 cP |
| Thermosetting mixed viscosity | | ASTMD2393 | 3750 cP |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 0.778 g/cm³ |
| density | | ASTMD1505 | 0.775 g/cm³ |
| density | | | 1.27 cm³/g |
| Shrinkage rate | | ASTMD2566 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 62 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WorkLife | | | 10.0到12.0 min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTMD790 | 1160 MPa |
| bending strength | | ASTMD790 | 23.4 MPa |
| compressive strength | | ASTMD695 | 19.1 MPa |
| tensile strength | | ASTMD638 | 14.9 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 130 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 62.8 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare