Unspecified BCC Resins DP-11-88 USA BCC Products
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | USA BCC Products/BCC Resins DP-11-88 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256 | 130 J/m |
Supplementary Information | Test Condition | Test Method | USA BCC Products/BCC Resins DP-11-88 |
---|---|---|---|
Applicable period | 24°C | 10.0to12.0 min |
hardness | Test Condition | Test Method | USA BCC Products/BCC Resins DP-11-88 |
---|---|---|---|
Shore hardness | 邵氏D | ASTM D2240 | 62 |
Mechanical properties | Test Condition | Test Method | USA BCC Products/BCC Resins DP-11-88 |
---|---|---|---|
tensile strength | ASTM D638 | 14.9 MPa | |
compressive strength | ASTM D695 | 19.1 MPa | |
Flexural modulus | ASTM D790 | 1160 MPa | |
bending strength | ASTM D790 | 23.4 MPa |
thermosetting | Test Condition | Test Method | USA BCC Products/BCC Resins DP-11-88 |
---|---|---|---|
Thermosetting mixed viscosity | --3 | ASTM D2393 | 4500 cP |
--4 | ASTM D2393 | 3750 cP | |
Thermosetting components | 部件A | 按重量计算的混合比:1.0 | |
Thermosetting mixed viscosity | --2 | ASTM D2393 | 3000 cP |
脱模时间5(24°C) | ASTM D2393 | 480to720 min | |
GelTime | ASTM D2471 | 12.0to14.0 min | |
Thermosetting components | 部件B | 按重量计算的混合比:1.0 |
physical property | Test Condition | Test Method | USA BCC Products/BCC Resins DP-11-88 |
---|---|---|---|
density | -- | ASTM D1505 | 0.775 g/cm³ |
Shrinkage rate | MD | ASTM D2566 | 0.10 % |
density | -- | ASTM D792 | 0.778 g/cm³ |
特定体积 | 1.27 cm³/g |
Thermal performance | Test Condition | Test Method | USA BCC Products/BCC Resins DP-11-88 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 62.8 °C |