ABS POLYLAC® PA-717CK
198
- Properties:Flame retardantThermal stabilitywear resistantHigh impact resistanceHigh rigidity
- Usages:Automotive sectorABS pipeElectrical enclosureElectrical appliances
- Certificates:ULMSDSSGS
Compare
View PricesTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 一般射出成型用 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 14 g/10min | |
| ASTM D-1238 | 1.4 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Izod notch impact strength | ASTM D256/ISO 179 | 25(4.6) kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 440（6,300） kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 25 % | |
| Rockwell hardness | ASTM D785 | R-115 | |
| Flexural modulus | ASTM D790/ISO 178 | 25000（35000） kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 720（10,200） kg/cm²(MPa)[Lb/in²] | |
| Izod notch impact strength | ASTM D256/ISO 179 | 27(5.2) kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D-790 | 720 kg/cm2 | |
| ASTM D-790 | 25 % | ||
| Flexural modulus | ASTM D-790 | 2.5 104kg/cm2 | |
| IZOD impact strength | ASTM D-256 | 25 kg.cm/cm | |
| ASTM D-256 | 28 kg.cm/cm | ||
| Rockwell hardness | ASTM D-785 | 115 R | |
| Tensile strength | ASTM D-638 | 450 kg/cm2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 1.4 g/10min | |
| ASTM D1238/ISO 1133 | 14 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL94 | 1/16 | |
| ASTM D648/ISO 75 | 99(210) ℃（℉） | ||
| ASTM D648/ISO 75 | 88(190) ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 105(221) ℃（℉） | |
| combustibility | File NO.E196075 | 1/16"HB | |
| ASTM D-648 | 98(208) ℃(°F) | ||
| ASTM D-648 | 87(189) ℃(°F) | ||
| vicat | ASTM D-1525 | 104(219) ℃(°F) |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.