ABS PA-717CK ZHENJIANG CHIMEI
POLYLAC®
Automotive sector、ABS pipe、Electrical enclosure、Electrical appliances
Flame retardant、Thermal stability、wear resistant、High impact resistance、High rigidity
UL
MSDS
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717CK |
|---|---|---|---|
| melt mass-flow rate | 200℃ 5kg | ASTM D-1238 | 1.4 g/10min |
| 200℃ 10kg | ISO 1133 | 14 g/10min |
| Mechanical properties | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717CK |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 27(5.2) kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 720（10.200） kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 25000（35000） kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 2.5 104kg/cm2 | ||
| elongation | ASTM D638/ISO 527 | 25 % | |
| Impact strength of cantilever beam gap | 1/8" | ASTM D-256 | 28 kg.cm/cm |
| tensile strength | ASTM D-638 | 450 kg/cm2 | |
| elongation at break | ASTM D-790 | 25 % | |
| bending strength | ASTM D-790 | 720 kg/cm2 | |
| Rockwell hardness | ASTM D785 | R-115 | |
| tensile strength | ASTM D638/ISO 527 | 440（6.300） kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 1/4" | ASTM D-256 | 25 kg.cm/cm |
| Rockwell hardness | ASTM D-785 | 115 R |
| other | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717CK |
|---|---|---|---|
| characteristic | 一般射出成型用 |
| Physical properties | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717CK |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 14 g/10min |
| Thermal performance | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717CK |
|---|---|---|---|
| Combustibility (rate) | UL 94 | 1/16 | |
| vicat | ASTM D-1525 | 104(219) ℃(°F) | |
| Heat distortion temperature | 退火，HDT | ASTM D-648 | 98(208) ℃(°F) |
| HDT | ASTM D648/ISO 75 | 88(190) ℃（℉） | |
| vicat | ASTM D1525/ISO R306 | 105(221) ℃（℉） | |
| Heat distortion temperature | 未退火，HDT | ASTM D-648 | 87(189) ℃(°F) |
| combustibility | File NO.E196075 | 1/16"HB |