PA6 Ultraflow K-FHG7 /A DSM Additive Manufacturing

Properties:
Filler
glass fiber reinforced material
35%
filler by weight
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate		ISO 294-4	1.00 %

Mechanical properties	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	70 kJ/m²
elongation at break		ISO 527-2	3.30 %
Tensile modulus		ISO 527-2	11000 MPa
bending strength		ISO 178	255 MPa
Flexural modulus		ISO 178	10000 MPa
Charpy Notched Impact Strength		ISO 179/1eA	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	95 kJ/m²
tensile strength		ISO 527-2	185 MPa

Flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 1.50mm

Electrical performance	Test Condition	Test Method	Test Result
dielectric constant		IEC 60250	3.30 1MHz
Dissipation Factor		IEC 60250	5E-03 100Hz
	Dissipation Factor		IEC 60250	0.015 1MHz
	Dissipation Factor	Dissipation Factor		IEC 60112	500 V
Volume resistivity		IEC 60093	>1.0E+15 Ω.cm
dielectric constant		IEC 60250	3.50 100Hz

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/Bf	220 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/Af	200 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.5E-05 cm/cm／°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	6E-05 cm/cm／°C
vicat	Melting Temperature	ISO 11357-3	220 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.