PA6 Ultraflow K-FHG7 /A DSM Additive Manufacturing
--
--
Filler, glass fiber reinforced material, 35%, filler by weight,
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodDSM Additive Manufacturing/ Ultraflow K-FHG7 /A
Hot deformation temperature0.45MPaUnannealedISO 75-2/Bf220 °C
1.80MPaAnnealedISO 75-2/Af200 °C
Linear coefficient of thermal expansionMDISO 11359-21.5E-05 cm/cm／°C
TDISO 11359-26E-05 cm/cm／°C
Vicat softening temperatureMelting TemperatureISO 11357-3220 °C
mechanical propertiesTest ConditionTest MethodDSM Additive Manufacturing/ Ultraflow K-FHG7 /A
Bending modulus23°CISO 17810000 MPa
bending strength23°CISO 178255 MPa
Charpy Notched Impact Strength-30°CISO 179/1eA12 kJ/m²
23°CISO 179/1eA15 kJ/m²
Elongation at Break23°CISO 527-23.30 %
Impact strength of simply supported beam without notch-30°CISO 179/1eU70 kJ/m²
23°CISO 179/1eU95 kJ/m²
Tensile modulus23°CISO 527-211000 MPa
tensile strength23°CISO 527-2185 MPa
flame retardant performanceTest ConditionTest MethodDSM Additive Manufacturing/ Ultraflow K-FHG7 /A
UL flame retardant ratingUL -94HB 1.50mm
Electrical performanceTest ConditionTest MethodDSM Additive Manufacturing/ Ultraflow K-FHG7 /A
Dielectric constant23°CIEC 602503.50 100Hz
23°CIEC 602503.30 1MHz
Dissipation factor相对漏电起痕指数IEC 60112500 V
23°CIEC 602505E-03 100Hz
23°CIEC 602500.015 1MHz
Volume resistivityIEC 60093>1.0E+15 Ω.cm
Physical propertiesTest ConditionTest MethodDSM Additive Manufacturing/ Ultraflow K-FHG7 /A
Shrinkage rateMDISO 294-40.30 %
TDISO 294-41.00 %