Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 10 kJ/m² |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/5 | 35.0 MPa |
| Tensile strain | | ISO527-2/5 | 0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 0.65to0.85 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 150 °C |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 9000 MPa |
| Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 3.23 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.65to0.85 % |
| Water absorption rate | | ISO62 | 0.040 % |
| | ISO75-2/A | 95.0 °C |
| Continuous use temperature | | | 110 °C |
| vicat | | ISO306/B50 | 160 °C |
| | ISO11359-2 | 2E-05 cm/cm/°C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 2.0 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare