Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 Latamid 12 CP/85 LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | LATI S.p.A./Latamid 12 CP/85 |
|---|---|---|---|
| tensile strength | 断裂,23°C | ISO 527-2/5 | 35.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 0.80 % |
| Test Condition | Test Method | LATI S.p.A./Latamid 12 CP/85 | |
|---|---|---|---|
| vicat | ISO 306/B50 | 160 °C | |
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.040 % |
| Continuous use temperature | 110 °C | ||
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.65to0.85 % |
| density | ISO 1183 | 3.23 g/cm³ | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C |
| Mechanical properties | Test Condition | Test Method | LATI S.p.A./Latamid 12 CP/85 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 150 °C |
| flammability | Test Condition | Test Method | LATI S.p.A./Latamid 12 CP/85 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.65to0.85 % |
| physical property | Test Condition | Test Method | LATI S.p.A./Latamid 12 CP/85 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 10 kJ/m² |
| elastomer | Test Condition | Test Method | LATI S.p.A./Latamid 12 CP/85 |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 9000 MPa |
| Thermal performance | Test Condition | Test Method | LATI S.p.A./Latamid 12 CP/85 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.0 kJ/m² |
Contact Us
Get App
Top