Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.44 g/cm³ |
| spiral flow length | | 内部方法 | 13.5 cm |
| Shrinkage rate | | ISO 294-4 | 0.50 % |
| Shrinkage rate | | ISO 294-4 | 0.0 % |
| Water absorption rate | | ISO 62 | 0.30 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 85 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ISO 11443 | 325 Pa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 85.0 MPa |
| tensile strength | | ISO 527-2 | 65.0 MPa |
| tensile strength | | ISO 527-2 | 55.0 MPa |
| Tensile strain | | ISO 527-2 | 1.8 % |
| tensile strength | | ISO 527-2 | 195 MPa |
| tensile strength | | ISO 527-2 | 125 MPa |
| compression stress | | ISO 604 | 160 MPa |
| compression stress | | ISO 604 | 65.0 MPa |
| compression stress | | ISO 604 | 45.0 MPa |
| Flexural modulus | | ISO 178 | 17000 MPa |
| bending strength | | ISO 178 | 290 MPa |
| bending strength | | ISO 178 | 220 MPa |
| bending strength | | ISO 178 | 140 MPa |
| bending strength | | ISO 178 | 70.0 MPa |
| compression stress | | ISO 604 | 230 MPa |
| Tensile modulus | | ISO 527-2 | 19500 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1U | 35 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 35 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+06 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 9E-06 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 3.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| thermal conductivity | | ISO 22007-4 | 1.3 W/m/K |
| thermal conductivity | | ISO 22007-4 | 2.2 W/m/K |
| melting temperature | | ISO 11357-3 | 343 °C |
| Heat distortion temperature | | ISO 75-2/Af | 343 °C |
| Glass Transition Temperature | | ISO 11357-2 | 143 °C |
| Glass Transition Temperature | | ISO 11357-2 | 147 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.