Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PAEK VICTREX® WG™ 101 VICTREX UK
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | VICTREX UK/VICTREX® WG™ 101 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 35 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1U | 35 kJ/m² |
| hardness | Test Condition | Test Method | VICTREX UK/VICTREX® WG™ 101 |
|---|---|---|---|
| Shore hardness | 邵氏D,23°C | ISO 868 | 85 |
| Electrical performance | Test Condition | Test Method | VICTREX UK/VICTREX® WG™ 101 |
|---|---|---|---|
| Volume resistivity | 23°C | IEC 60093 | 1E+06 ohms·cm |
| Mechanical properties | Test Condition | Test Method | VICTREX UK/VICTREX® WG™ 101 |
|---|---|---|---|
| tensile strength | 断裂,125°C | ISO 527-2 | 125 MPa |
| compression stress | 250°C | ISO 604 | 45.0 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 19500 MPa |
| tensile strength | 断裂,225°C | ISO 527-2 | 65.0 MPa |
| 断裂,275°C | ISO 527-2 | 55.0 MPa | |
| compression stress | 120°C | ISO 604 | 160 MPa |
| bending strength | 125°C | ISO 178 | 220 MPa |
| Flexural modulus | 23°C | ISO 178 | 17000 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.8 % |
| bending strength | 175°C | ISO 178 | 140 MPa |
| compression stress | 23°C | ISO 604 | 230 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 195 MPa |
| bending strength | 275°C | ISO 178 | 70.0 MPa |
| compression stress | 200°C | ISO 604 | 65.0 MPa |
| tensile strength | 断裂,175°C | ISO 527-2 | 85.0 MPa |
| bending strength | 23°C | ISO 178 | 290 MPa |
| Filling analysis | Test Condition | Test Method | VICTREX UK/VICTREX® WG™ 101 |
|---|---|---|---|
| melt viscosity | 400°C | ISO 11443 | 325 Pa·s |
| physical property | Test Condition | Test Method | VICTREX UK/VICTREX® WG™ 101 |
|---|---|---|---|
| spiral flow length | 内部方法 | 13.5 cm | |
| Shrinkage rate | TD | ISO 294-4 | 0.50 % |
| MD | ISO 294-4 | 0.0 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| 100°C，饱和 | ISO 62 | 0.60 % | |
| density | ISO 1183 | 1.44 g/cm³ |
| Thermal performance | Test Condition | Test Method | VICTREX UK/VICTREX® WG™ 101 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD:>143°C | ISO 11359-2 | 1E-05 cm/cm/°C |
| thermal conductivity | 23°C9 | ISO 22007-4 | 2.2 W/m/K |
| melting temperature | ISO 11357-3 | 343 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 343 °C |
| thermal conductivity | 23°C8 | ISO 22007-4 | 1.3 W/m/K |
| Linear coefficient of thermal expansion | MD:<143°C | ISO 11359-2 | 9E-06 cm/cm/°C |
| TD:>143°C | ISO 11359-2 | 8.5E-05 cm/cm/°C | |
| Glass Transition Temperature | --6 | ISO 11357-2 | 143 °C |
| --7 | ISO 11357-2 | 147 °C | |
| Linear coefficient of thermal expansion | TD:<143°C | ISO 11359-2 | 3.5E-05 cm/cm/°C |
Contact Us