HDPE PRE-ELEC® PE 1294
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD792 | 0.996 g/cm³ | |
| ISO1183 | 1.01 g/cm³ | ||
| melt mass-flow rate | ASTMD1238 | 20 g/10min | |
| ASTMD1238 | 2.0 g/10min | ||
| ASTMD1238 | 80 g/10min | ||
| ISO1133 | 20 g/10min | ||
| ISO1133 | 2.0 g/10min | ||
| ISO1133 | 80 g/10min | ||
| Shrinkage rate | ASTMD955 | 1.5to2.5 % | |
| ISO294-4 | 1.5to2.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore A | ASTMD2240 | 95 | |
| ASTMD2240 | 66 | ||
| Shore A | ISO868 | 95 | |
| ISO868 | 66 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO178 | 1000 MPa | |
| tensile strength | Yield | ASTMD638 | 23.0 MPa |
| Tensile stress | Yield | ISO527-2 | 23.0 MPa |
| tensile strength | ISO527-2 | 12.0 MPa | |
| elongation | Yield | ASTMD638 | 15 % |
| Tensile strain | Yield | ISO527-2 | 15 % |
| elongation | Break | ASTMD638 | 300 % |
| Tensile strain | ISO527-2 | 300 % | |
| Flexural modulus | ASTMD790 | 1000 MPa | |
| tensile strength | ASTMD638 | 12.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| CharpyNotchedImpactStrength | ASTMD256 | 8.4 kJ/m² | |
| Impact strength of cantilever beam gap | ISO180 | 12 kJ/m² | |
| Suspended wall beam without notch impact strength | ASTMD256 | NoBreak | |
| ASTMD256 | NoBreak | ||
| ISO180 | NoBreak | ||
| ISO180 | NoBreak | ||
| Impact strength of simply supported beam without notch | ISO179 | NoBreak | |
| ASTMD256 | NoBreak | ||
| NotchedIzodImpact(Area) | ASTMD256 | 4.20 kJ/m² | |
| ASTMD256 | 12.6 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO180 | 4.0 kJ/m² | |
| CharpyNotchedImpactStrength | ISO179 | 10 kJ/m² | |
| ISO179 | 15 kJ/m² | ||
| ASTMD256 | 15 kJ/m² | ||
| Impact strength of simply supported beam without notch | ASTMD256 | NoBreak | |
| ISO179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ESDSTM11.11 | <1.0E+5 ohms | |
| IEC61340-2-3 | <1.0E+5 ohms | ||
| Volume resistivity | 内部方法 | <1.0E+4 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/Bf | 76.0 °C | ||
| ASTMD648A | 45.0 °C | ||
| ISO75-2/Af | 45.0 °C | ||
| vicat | ISO306/A50 | 125 °C | |
| ISO306/B50 | 63.0 °C | ||
| ASTMD648B | 76.1 °C | ||
| vicat | ASTMD15253 | 125 °C | |
| ASTMD15254 | 62.8 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.