HDPE PRE-ELEC® PE 1294 Premix Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PE 1294
Charpy Notched Impact Strength-20°CASTM D2568.4 kJ/m²
Impact strength of cantilever beam gap23°CISO 18012 kJ/m²
Charpy Notched Impact Strength23°CASTM D25615 kJ/m²
Impact strength of cantilever beam gap-20°CISO 1804.0 kJ/m²
Suspended wall beam without notch impact strength-20°C,4.00mmASTM D256NoBreak
Impact strength of simply supported beam without notch23°CASTM D256NoBreak
-20°CASTM D256NoBreak
-20°CISO 179NoBreak
Charpy Notched Impact Strength23°CISO 17915 kJ/m²
Suspended wall beam without notch impact strength-20°CISO 180NoBreak
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Impact strength of cantilever beam gap-20°C,4.00mm，AreaASTM D2564.20 kJ/m²
23°C,4.00mm，AreaASTM D25612.6 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180NoBreak
Charpy Notched Impact Strength-20°CISO 17910 kJ/m²
Suspended wall beam without notch impact strength23°C,4.00mmASTM D256NoBreak
hardnessTest ConditionTest MethodPremix Oy/PRE-ELEC® PE 1294
Shore hardness邵氏DASTM D224066
邵氏DISO 86866
邵氏AISO 86895
邵氏AASTM D224095
Mechanical propertiesTest ConditionTest MethodPremix Oy/PRE-ELEC® PE 1294
elongation断裂ASTM D638300 %
屈服ASTM D63815 %
tensile strength ASTM D63812.0 MPa
Tensile strain屈服ISO 527-215 %
断裂,4.00mmISO 527-2300 %
Flexural modulus4.00mmISO 1781000 MPa
4.00mmASTM D7901000 MPa
tensile strength 屈服ASTM D63823.0 MPa
屈服ISO 527-223.0 MPa
4.00mmISO 527-212.0 MPa
Electrical performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PE 1294
Surface ResistivityESDSTM11.11<1.0E+5 ohms
IEC 61340-2-3<1.0E+5 ohms
Volume resistivity内部方法<1.0E+4 ohms·cm
physical property Test ConditionTest MethodPremix Oy/PRE-ELEC® PE 1294
melt mass-flow rate190°C/10.0kgASTM D123820 g/10min
190°C/21.6kgASTM D123880 g/10min
Shrinkage rateMDASTM D9551.5to2.5 %
MDISO 294-41.5to2.5 %
melt mass-flow rate190°C/10.0kgISO 113320 g/10min
densityASTM D7920.996 g/cm³
ISO 11831.01 g/cm³
melt mass-flow rate190°C/2.16kgASTM D12382.0 g/10min
190°C/2.16kgISO 11332.0 g/10min
190°C/21.6kgISO 113380 g/10min
Thermal performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PE 1294
Heat distortion temperature1.8MPa,未退火，HDTASTM D648A45.0 °C
1.8MPa,未退火，HDTISO 75-2/Af45.0 °C
0.45MPa,未退火，HDTASTM D648B76.1 °C
vicat--ISO 306/A50125 °C
--ASTM D15253125 °C
--ASTM D1525462.8 °C
--ISO 306/B5063.0 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/Bf76.0 °C