TPE DuraGrip® DGR 6070NC
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.2 % | |
| ISO 294-4 | 1.1 % | ||
| ISO 294-4 | 2.1 % | ||
| ISO 294-4 | 1.2 % | ||
| ISO 294-4 | 1.3 % | ||
| ASTM D955 | 1.1 % | ||
| ASTM D955 | 1.3 % | ||
| ASTM D955 | 2.1 % | ||
| density | ISO 1183 | 0.988 g/cm³ | |
| ASTM D792 | 0.988 g/cm³ | ||
| MeltViscosity | ASTM D3835 | 104 Pa·s |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 68 | |
| ASTM D2240 | 68 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Taber wear resistance | ASTM D1044 | 10.0 mg |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | Break | ASTM D412 | 370 % |
| ISO 37 | 370 % | ||
| Stretch permanent deformation | ASTM D412 | 15 % | |
| tensile strength | ASTM D412 | 1.67 MPa | |
| ISO 37 | 1.67 MPa | ||
| ASTM D412 | 7.83 MPa | ||
| ISO 37 | 7.83 MPa | ||
| tear strength | ASTM D624 | 26.1 kN/m | |
| compression set | ASTM D395B | 27 % | |
| ASTM D395B | 45 % | ||
| ASTM D395B | 72 % | ||
| ISO 815 | 27 % | ||
| ISO 815 | 72 % | ||
| ISO 815 | 45 % |
| aging | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume change | ISO 1817 | -7.0 % | |
| ISO 1817 | 2.0 % | ||
| ISO 1817 | 38 % | ||
| Change rate of tensile strength in air | ISO 188 | -4.0 % | |
| ISO 188 | -11 % | ||
| ISO 188 | -2.0 % | ||
| Change rate of ultimate elongation in air | ASTM D573 | 2.0 % | |
| ASTM D573 | 3.0 % | ||
| volume change | ASTM D471 | 38 % | |
| ASTM D471 | -7.0 % | ||
| ISO 1817 | 9.0 % | ||
| Change rate of tensile strength in air | ASTM D573 | -11 % | |
| ASTM D573 | -2.0 % | ||
| ISO 188 | -9.0 % | ||
| ASTM D573 | -4.0 % | ||
| ASTM D573 | -9.0 % | ||
| volume change | ASTM D471 | 2.0 % | |
| ASTM D471 | 9.0 % | ||
| Tensile stress change rate | ISO 1817 | 3.0 % | |
| ISO 1817 | 2.0 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| brittle temperature | ISO 812 | -65.0 °C | |
| ASTM D746 | -65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.